Abstract:

Fracture of highly stretched materials challenges our view of how things break. We directly visualize rupture of tough double-network gels at >50% strain. During fracture, crack tip shapes obey a x∼y1.6 power law, in contrast to the parabolic profile observed in low-strain cracks. A new length scale â.," emerges from the power law; we show that â.," scales directly with the stored elastic energy and diverges when the crack velocity approaches the shear wave speed. Our results show that double-network gels undergo brittle fracture and provide a testing ground for large-strain fracture mechanics.

Notes: